 產(chǎn)品詳細(xì)介紹 |
|
項 目 \ 牌 號 |
硅磚 |
粘土質(zhì) |
特種高鋁質(zhì) |
堇青石質(zhì) |
|
|
|
JNLA |
JN40a |
JN40b |
BGZ-65 |
BGZ-70 |
JLZ-75 |
JHL-75 |
SDHA60S |
|
| Al2O3 % |
≤1.5 |
30～36
|
≥40 |
≥40 |
|
|
≥75 |
≥75 |
≥60 |
≥40 |
| Fe2O3 % |
≤1.5 |
≤2.5 |
≤2.0 |
≤2.0 |
|
|
|
≤0.8 |
≤1.5 |
|
| SiO2 % |
≥94.5 |
|
|
|
≥65 |
≥70 |
|
|
|
|
| K2O+Na2O % |
CaO≤2.5 |
|
|
|
|
|
|
≤0.5 |
|
MgO≥3 |
| 耐火度 ℃ |
|
≥1690 |
≥1730 |
≥1730 |
|
|
≥1790 |
≥1790 |
≥1790 |
≥1580 |
荷重軟化溫度 ℃
|
KD≥1650 |
|
Ta≥1450 |
Ta≥1400 |
Ta≥1320 |
Ta≥1350 |
KD≥1550 |
KD≥1650 |
Ta≥1640 |
|
重?zé)�變化率 %
|
1450℃×2h
0～+0.2
|
|
|
|
|
|
1500℃×2h
+0.1～-0.4
|
1500℃×2h
0～+0.3 |
|
1300℃×2h
0.7 |
顯氣孔率 %
|
≤22 |
≤24 |
≤24(22) |
≤20 |
≤24 |
≤22(24) |
≤21(23) |
≤20 |
≤18 |
≤20 |
≤30 |
體積密度 g/cm3
|
真密度
≤2.33 |
真密度
≤2.34 |
≥2.0 |
≥2.0 |
≥2.0 |
|
|
|
≥2.65 |
≥2.4 |
|
常溫耐壓強(qiáng)度 MPa
|
≥40 |
≥35 |
≥25(20) |
≥35 |
≥30 |
≥35(25) |
≥40(30) |
≥65 |
≥90 |
≥50 |
≥15 |
熱震穩(wěn)定性,次(1100℃ 水冷)
|
|
|
|
|
|
|
|
|
≥35 |
≥20
(DIN51068) |
≥20 |
殘余石英 %
|
≤1.0 |
|
|
|
|
|
|
|
熱膨脹率(參考) %
(1000℃) |
≤1.28 |
≤1.30 |
|
≤0.6 |
≤0.6 |
|
|
|
|
≤0.6 |
|
| 用 途 |
爐底、爐壁 |
其它
|
蓄熱室大墻、格子磚
|
炭化室、燃燒室
|
爐門
| | | |
|